ANYCUBIC ABS-Like Resin 3.0 is a photopolymer resin for LCD and DLP 3D printers, offering high mechanical strength, crack resistance, and very precise print details. Thanks to low shrinkage, low viscosity, and minimal odor, it is comfortable to work with and suitable for creating durable models with a smooth surface. The price is for 1 piece (1 kg).
ANYCUBIC ABS-Like Resin 3.0 (black) is a resin designed for users who need not only a great look from prints, but also durability in everyday use. The material features hardness 83–86 HD, impact toughness 130 J/m, and elongation at break 25–30%, making models less prone to cracking and better able to withstand stress (e.g., during drilling or minor machining).
Thanks to low volumetric shrinkage (3.9–4.9%) and optimized viscosity of 280–300 mPa·s, the resin achieves high accuracy and a smooth surface. Good flow also helps speed up the material’s return into the print area, which can contribute to shorter print time and higher productivity.
The resin is compatible with a wide range of LCD and DLP printers using UV light in the 365–405 nm range. The formulation is developed with odor minimization and greater working comfort in mind. It is sold as 1 piece (a bottle with a weight of 1 kg).
- Suitable use: mechanical parts, device covers, components exposed to stress
- Precise details: low shrinkage and optimized viscosity
- Wide compatibility: LCD/DLP, 365–405 nm
Specifications
- Manufacturer
- ANYCUBIC
- Model
- ABS-Like 3.0
- Color
- Black
- Material
- Photopolymer resin
- Wavelength
- 365–405 nm
- Viscosity
- 280–300 mPa·s (25 °C)
- Density
- 1.06–1.09 g/cm³
- Hardness
- 83–86 HD
- Tensile strength
- 38–45 MPa
- Elongation at break
- 25–30 %
- Flexural modulus of elasticity
- 50–65 MPa
- Flexural strength
- 1500–2000 MPa
- Young’s modulus
- 1300–1700 MPa
- Izod impact toughness
- 130 J/m
- Volumetric shrinkage
- 3.9–4.9 %
- Printing temperature
- 20–50 °C
- Recommended ambient temperature during printing
- 20–40 °C
- First layer exposure time
- 23–40 s
- Standard layer exposure time
- 2–3.6 s
- Cleaning agent
- 95% IPA
- Washing time
- ≥3 min
- UV wavelength during curing
- 405 nm
- Curing temperature
- 18–30 °C
- UV intensity
- 25,000–30,000 µW/cm²
- Curing time
- 3 min