ANYCUBIC ABS-Like Resin Pro 2 is an ABS-like photopolymer resin for LCD/DLP 3D printing, designed for high mechanical strength, damage resistance, and precise details. Thanks to an elongation at break of 35–40%, it is more flexible and less prone to cracking, while maintaining low shrinkage and good fluidity for efficient printing.
ABS-Like Resin Pro 2 (transparent) was developed for applications where a combination of strength and elasticity is important. You will use it for printing structural parts, handles, assembly jigs, and industrial prototypes – anywhere standard resins may crack more easily.
The material features low viscosity and good flow, which contributes to faster layer curing and more stable results. Good adhesion to the build plate helps reduce the risk of failed prints, and a low shrinkage rate supports accurate detail reproduction and a smooth surface.
Main advantages:
- Higher resistance to deformation and damage
- Flexibility thanks to 35–40% elongation at break
- Reduced odor intensity for more comfortable work
- Compatibility with LCD and DLP printers (UV 365–405 nm), optimized for Anycubic LCD
Specifications
- Manufacturer
- ANYCUBIC
- Model
- ABS-Like Resin Pro 2
- Color
- Transparent
- Material
- Photopolymer resin
- Wavelength
- 365–405 nm
- Viscosity
- 300–400 mPa·s (25 °C)
- Density
- 1.05–1.25 g/cm³
- Hardness
- 82–84 HD
- Tensile strength
- 35–45 MPa
- Elongation at break
- 35–40%
- Flexural modulus
- 40–45 MPa
- Flexural strength
- 1 400–1 800 MPa
- Young’s modulus
- 1 600–1 800 MPa
- Izod impact strength
- 212 J/m
- Volumetric shrinkage
- 4.3–5.6%
- Printing temperature
- 20–50 °C
- Recommended ambient temperature during printing
- 20–40 °C
- First layer exposure time
- 20–40 s
- Standard layer exposure time
- 1.5–3 s
- Cleaning agent
- 95% IPA
- Washing time
- ≥ 3 min
- UV curing wavelength
- 405 nm
- Curing temperature
- 18–30 °C
- UV intensity
- 25 000–30 000 µW/cm²
- Curing time
- 3 min